EAA膠料/美國(guó)陶氏/3460 擠壓涂膜EAA樹(shù)脂原料
產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min |
| 熔體流動(dòng)速率 | 190℃/2.16kg | ISO 1133 | 20 | g/10min | |
| 單體含量 | Internal Method | 9.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.938 | g/cm3 | |
| 比重 | ISO 1183 | 0.938 | g/cm3 | ||
| 機(jī)械性能 | 拉伸屈服強(qiáng)度 | Compression Molded | ASTM D-638 | 7.24 | MPa |
| 拉伸屈服強(qiáng)度 | Compression Molded | ISO 527-2 | 7.24 | MPa | |
| 拉伸斷裂強(qiáng)度 | Compression Molded | ASTM D-638 | 16.2 | MPa | |
| 拉伸斷裂強(qiáng)度 | Compression Molded | ISO 527-2 | 16.2 | MPa | |
| 拉伸斷裂伸長(zhǎng)率 | Compression Molded | ASTM D-638 | 580 | % | |
| 拉伸斷裂伸長(zhǎng)率 | Compression Molded | ISO 527-2 | 580 | MPa | |
| 加工性能 | 熔體溫度 | 220-260 | ℃ | ||
| 熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 72.2 | ℃ | |
| 維卡軟化點(diǎn) | ISO 306 | 72.2 | ℃ | ||
| 熔融溫度 | Internal Method | 95 | ℃ | ||
| 其它性能 | 密封起始溫度 | Internal Method | 85 | ℃ | |
| 水汽傳輸速率 | 38℃，90% RH | DIN 53122/2 | 0.44 | g·mm/m2/atm/24hr | |
EAA膠料/美國(guó)陶氏/3460 擠壓涂膜EAA樹(shù)脂原料
| Physical | Nominal Value | Unit | Test Method |
Specific Gravity | |||
-- | 0.940 | ASTM D792 | |
-- | 0.938 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
Comonomer Content 2 | 9.7 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength | ASTM D638, ISO 527-2 | ||
Yield, Compression Molded | 1050 | psi | |
Break, Compression Molded | 2350 | psi | |
Tensile Elongation (Break, Compression Molded) | 580 | % | ASTM D638, ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
Seal Initiation Temperature 3 | 185 | °F | Internal Method |
Water Vapor Transmission Rate (100°F, 90% RH) | 1.1 | g·mil/100in2/atm/24 hr | DIN 53122/2 |
| Thermal | Nominal Value | Unit | Test Method |
Vicat Softening Temperature | 162 | °F | ASTM D1525, ISO 306 |
Melting Temperature (DSC) | 203 | °F | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
Melt Temperature | 428 to 500 | °F | |
Minimum Coating Thickness | 0.40 | mil | Internal Method |
Minimum Coating Weight | 6.0 | lb/ream | Internal Method |
Neck-in (550°F, 1.0 mil) | 2.8 | in | Internal Method |
EAA廣泛應(yīng)用：
EAA食品油包裝、EAA肉類包裝、EAA牙膏軟管；
EAA液體包裝袋、EAA食品包裝袋、EAA電纜屏蔽層；
EAA無(wú)紡布涂層、EAA膠黏劑、EAA包裝袋、EAA電纜屏蔽層；
EAA無(wú)紡布涂層、EAA電纜屏蔽層環(huán)保降解材料；
EAA膠黏劑、EAA涂料應(yīng)用、EAA層板、EAA擠出級(jí)；
EAA膠黏劑、EAA涂料應(yīng)用、EAA薄片、EAA油管；
EAA鋁或紙的超薄涂層、EAA非織造布的結(jié)構(gòu)層、EAA熱熔膠；
EAA擠出級(jí)、EAA膠黏劑、EAA涂層應(yīng)用、EAA層板；
EAA鋁或紙的超薄涂層、EAA水性粘接劑、EAA熱熔膠